PRIMERS
EVA PRIMER
DRYING TIME: 20 MINField of use: EVA PRIMER is used to allow better bonding of EVA materials, without roughing, after washing with solvent (B-SOLV- 151 P or B-SOLV 141 F), usually with polyurethane adhesives. EVA PRIMER is also suitable to be used as a primer for Micro soles (also with oxidized soles). This product does not yellow over time.
Application: EVA PRIMER is normally used by brush (can also be applied by spray or immersion). Let dry or about 20 minutes.
B-PUR 136 PRIMER
VISCOSITY: LOWDRYING TIME: 5 – 15 MIN
Field of use: B-PUR 136 PRIMER is used as a primer on oiled leather and on those materials that are difficult to process, with the purpose of improving the bonding of polyurethane adhesives. B-PUR 136 PRIMER is usually used with
5-7% activator.
Application: B-PUR 136 PRIMER is applied by brush on the upper. For oiled leathers, it is necessary to add 5-7% activator.
Application: B-PUR 136 PRIMER is applied by brush on the upper. For oiled leathers, it is necessary to add 5-7% activator.
B-PUR 835 N
VISCOSITY: LOWDRYING TIME: 2 H
Field of use: B-PUR 835 N is mainly used to facilitate the adhesion of polyurethane castings on rubber or TR. Activator can be added to B-PUR 835 N.
Application: Apply by spray or brush on rubber or TR previously halogenated with B-CLOR T3. Let dry for at least two hours then heat the surface and proceed to the casting.
Application: Apply by spray or brush on rubber or TR previously halogenated with B-CLOR T3. Let dry for at least two hours then heat the surface and proceed to the casting.
B-PREN 753 C
VISCOSITY: HIGHDRYING TIME: 10 – 20 MIN
Field of use: B-PREN 753 C is a polychloroprene primer, particularly used on compact, therefore poorly absorbent surfaces.
Application: B-PREN 753 C is usually applied by brush and, where necessary, it must be mixed with activator.
Application: B-PREN 753 C is usually applied by brush and, where necessary, it must be mixed with activator.
PRIMER UV
VISCOSITY: LOWDRYING TIME: 15 MIN
Field of use: PRIMER UV allows the bonding of EVA materials without prior roughing, by washing with a special solvent (B-SOLV 151 P or B-SOLV 141 F) and by exposing the processed materials to radiation through a specific UV machine. This product does not yellow over time.
Application: PRIMER UV can be applied by brush or spray. Once the surface of the EVA material has been thoroughly cleaned, apply UV PRIMER, after about 15 min expose the material to radiation through a specific UV oven and after short cooling (about 5 min) apply a polyurethane adhesive.
Application: PRIMER UV can be applied by brush or spray. Once the surface of the EVA material has been thoroughly cleaned, apply UV PRIMER, after about 15 min expose the material to radiation through a specific UV oven and after short cooling (about 5 min) apply a polyurethane adhesive.
B-735 TR
VISCOSITY: LOWDRYING TIME: 25 – 35 MIN
Field of use: B 735 TR is used in TR injection processes on leather, tunit and micro.
Application: B 735 TR is usually applied by brush or roller. The processed material must then be inserted into the mould ready for TR injection.
Application: B 735 TR is usually applied by brush or roller. The processed material must then be inserted into the mould ready for TR injection.
B-36 PRIMER
VISCOSITY: MEDIUMDRYING TIME: 23 – 35 MIN
Field of use: B-36 PRIMER is used to facilitate the adhesion of polystyrene surfaces with polyurethane adhesives.
Application: Apply B-36 PRIMER with a brush on the surface to be prepared for bonding.
Application: Apply B-36 PRIMER with a brush on the surface to be prepared for bonding.
HALOGENATING SOLUTIONS
B-CLOR T 3
DRYING TIME: 30 MIN
Field of use: B-CLOR T 3 is used for the surface treatment
(halogenation) of materials such as TR and SBR vulcanised
rubber before bonding with polyurethane adhesives.
Application: B-CLOR T 3 is usually applied by brush. Let dry for about 30 min. For light-colored soles, we recommend to test the product previously.
Application: B-CLOR T 3 is usually applied by brush. Let dry for about 30 min. For light-colored soles, we recommend to test the product previously.
SOLVENTS and THINNERS
B-SOLV 151 P
Feild of use: B-SOLV 151 P is a solvent mixture typically used for cleaning EVA, TPU, PU, PVC, SBR vulcanized rubber soles. This mixture of solvents can also be used for the dilution of polyurethane and polychloroprene adhesives, for
cleaning brushes, moulds and machinery.
B-SOLV 141 F
Field of use: B-SOLV 141 F is a solvent mixture particularly
suitable for cleaning EVA, TPU, PVC, SBR vulcanized rubber
soles. This solvent mixture can also be used for the dilution
of polyurethane adhesives.
ECO SMACCHIATORE
DRYING TIME: 10 MIN
Field of use: ECO SMACCHIATORE is mainly used in the shoe-finishing phase. It is a light solvent, so it can be used to clean the uppers of finished shoes. It is also used in sole factories, to clean TR funds after moulding.
Application: When cleaning uppers, ECO SMACCHIATORE is usually applied with cotton or a rag, repeatedly rubbing where needed. When cleaning TR soles, we recommend to use a rag.
Application: When cleaning uppers, ECO SMACCHIATORE is usually applied with cotton or a rag, repeatedly rubbing where needed. When cleaning TR soles, we recommend to use a rag.